Your present location:HOME >> Products >> Petroleum Machinery >> Tungsten Alloy Anticorrosive and Wear-resistant Casing and Anticorrosive Liner Pipe
  • Product Name: Tungsten Alloy Anticorrosive and Wear-resistant Casing and Anticorrosive Liner Pipe
  • Views : 131

1. Structure:

There is deposition of tungsten alloy layer on inner and outer walls of API standard pipes. Liner pipes are perforated on the 

casing backing material

 (called liner pipes after drilling), and there are deposition of tungsten alloy layer on inner and outer walls of pipes.

 2. Performance Indicators:

Mechanical Property: The pipe meets API Standards

Anticorrosion Property: Resistance to H2S/CO2 corrosion in high temperature, salt water corrosion, alkali corrosion 

and weak acid corrosion, 

meeting the corrosion resistance requirements of NACE 0177 Standards.

Wear Resistance: Good, equivalent to that of hard chromium layer.

Hardness of Tungsten Alloy Layer: ≥650HV

Tungsten Alloy Layer and Backing Material Binding Force: According to GB/T5270-2005 testingthe plating

 layer does not crack or peel off.

Threaded Connection: The threads are of good resistance to thread gluing.

Appearance: Uniformly bright, showing silvery white

Thickness of Tungsten Alloy Layer: ≥60μm

 3. Performance Testing

Wear and Corrosion Resistance Test: Passed a variety of the wear and corrosion resistance test carried out by Xi'an CNPC 

Tubular Goods 

Research Institute, Xi’an Maurer Petroleum Engineering Laboratory, and Quality Supervision and Inspection Center of Surface Covering 

Layer Products for Machinery Industry.

Gas Seal Test: Passed the gas seal test of Xi'an CNPC Tubular Goods Research Institute.

Corrosion Detection Test in Yuanba Gas Field (Xi'an Maurer Petroleum Engineering Laboratory)

 

Test Item

Test Standards

Testing Organization

Corrosion Rate

Corrosion Morphology

NACE RP-0775-2005

Xi’an Maurer Petroleum Engineering Laboratory

Conclusion

In simulated Yuanba corrosive environmental conditions (partial pressure of H2S: 5MPa, partial pressure of CO2

11MPa, elemental sulfur content: 10g/L, 

chloride ion content: 80000mg/L, temperature: 160), the uniform corrosion rates of 1# and 2# samples are 

0.0119mm/a and 0.0076mm/a respectively

the uniform corrosion is mild, and no obvious local corrosion appears on the surface of the samples.

In simulated corrosive environmental conditions of residual acid flowback (partial pressure of H2S: 5MPa, 

partial pressure of CO2: 11MPa; corrosive medium: 

residual acid prepared by Southwest Oil and Gas Field Engineering Institute, with PH value adjusted to 4.0;

 temperature160), the uniform corrosion rates of

 the samples are 0.0069mm/a, the uniform corrosion is mild, and no obvious local corrosion appear

on the surface of the samples.

All rights reserved:Hunan Nanofilm New Material Technology Co.,Ltd.  湘ICP备09027425号 Power by:www.300.cn   |  manager湘公网安备 43011202000415号

Address: 5th Floor, Dongta Building, Hunan Chamber of Commerce MansionNo.569, 3rd Section of Furong Middle Road, Yuhua District, Changsha City, Hunan ,P.R.China.

Tungstem Alloy Tubing,Tungsten Alloy Casing,Tungsten Alloy Drill Pipe,Sucker Rod Coupling,Condensation Cooler,Downhole Motor,Injection Screw,Pipe Coupling